Atlas carries C10100 Oxygen Free High Conductivity Copper (OFHC) Sheet / Plate in a wide range of sizes and will cut the material to length.
C10100 OFHC Copper is produced by the direct conversion of selected refined
cathodes and castings under carefully controlled conditions to prevent
contamination of the pure oxygen-free metal
during processing. The method of producing OFHC copper ensures extra
high grade of metal with a copper content of 99.99%. With so small a
content of extraneous elements, the inherent properties of elemental
copper are brought forth to a high degree.
Transistor Component Bases, High Resistance-Ratio Cryogenic Shunts, Bus
Conductors, Wave Guides, Hollow Conductors, Anodes for Vacuum Tubes,
Coaxial Cable, Coaxial Tube, Klystrons, Microwave Tubes, Bus Bars,
Lead-in Wire, Vacuum Seals, Conductors, Glass-to-Metal Seals
CHEMICAL COMPOSITION
(%max., unless shown as range or min.) NOTE: Information courtesy copper.org
Cu(1)
Sb
As
O
P
Te
Min./Max.
99.99 min
.0004
.0005
.0005
.0003
.0002
Nominal
-
-
-
-
-
-
(1) Cu is determined by the difference between the impurity total and 100%. The Cu value is exclusive of Ag. Note:
This is a high conductivity copper which has, in the annealed condition
a minimum concuctivity of 100% IACS except for Alloy C10100 which has a
minimum conductivity of 101% IACS.
Note: The following additional
impurity maximum limits shall apply: Bi, 1ppm (.0001%); Cd, 1ppm
(.0001%); Fe, 10ppm (.0010%); Pb, 5ppm (.0005%); Mn, 0.5ppm (.00005%);
Ni, 10ppm (.0010%); Se, 3ppm (.0003%); Ag, 25ppm(.0025%);S, 15ppm
(.0015%); Sn, 2ppm (.0002%); Zn, 1ppm (.0001%).
MECHANICAL PROPERTIES (measured at room temperature, 68 F (20 C) NOTE: Information courtesy copper.org