C63000 Nickel Aluminum Solid Bar
Atlas carries
C63000 Nickel Aluminum Bronze Solid Bar per ASTM B150, ASME SB150, AMS 4640, QQ-C-465 in stock. We carry a very large range of sizes and will cut the
material to length.
C63000 Nickel Aluminum Bronze is an extruded or forged Wrought Alloy that contains Nickel (nominal 5%). As an aluminum bronze, C63000 has excellent resistance to saltwater corrosion and displays exceptionall
strength and toughness as well. C63000 is typically used where higher mechanical properties are required. It is used in
equipment for marine applications, such as: valve stems, high
strength bushings, valve guides and seats, gears, cams, ship propellers,
as well as propeller nuts and shafts.
Aluminum Bronzes are most commonly used in water applications because of their
great resistance to corrosion in a
variety of water environments. This makes them preferable to other engineering materials.
Available from your C63000 Nickel Aluminum Bronze supplier in the following sizes:
Diameter (inches)
|
Part Number
|
|
.3750"
|
6300S-3
|
|
.4375"
|
6300S-3.5
|
|
.5000"
|
6300S-4
|
.5625"
|
6300S-4.5
|
|
.6250"
|
6300S-5
|
|
.6875"
|
6300S-5.5
|
|
.7500"
|
6300S-6
|
|
.8125"
|
6300S-6.5
|
|
.8750"
|
6300S-7
|
|
.9375"
|
6300S-7.5
|
|
1.000"
|
6300S-8
|
|
1.125"
|
6300S-9
|
1.1875"
|
6300S-9.5
|
1.250"
|
6300S-10
|
|
1.375"
|
6300S-11
|
1.500"
|
6300S-12
|
1.625"
|
6300S-13
|
1.750"
|
6300S-14
|
1.875"
|
6300S-15
|
2.000"
|
6300S-16
|
|
2.125"
|
6300S-17
|
2.250"
|
6300S-18
|
2.375"
|
6300S-19
|
|
2.500"
|
6300S-20
|
2.625"
|
6300S-21
|
2.750"
|
6300S-22
|
|
3.000"
|
6300S-24
|
3.250"
|
6300S-26
|
3.500"
|
6300S-28
|
3.750"
|
6300S-30
|
|
4.000"
|
6300S-32
|
4.250"
|
6300S-34
|
4.500"
|
6300S-36
|
4.750"
|
6300S-38
|
5.000"
|
6300S-40
|
|
5.750"
|
6300S-46
|
6.000"
|
6300S-48
|
6.500"
|
6300S-52
|
7.000"
|
6300S-56
|
7.500"
|
6300S-60
|
8.000"
|
6300S-64
|
9.000"
|
6300S-72
|
10.00"
|
6300S-80
|
TYPICAL USES:
Some of the typical areas that C63000 is used in, is as follows: Valve Seats, Plunger Tips, Condenser Tube for Power Stations and
Desalting Units, Shafting, Pump Parts, Cams, Gears, Valve Guides,
Aircraft Parts, Pump Shafts, Structural Members, Corrosion Resistant
Articles, Hydraulic Bushings for Earth Moving Equipment, Valve Balls,
Bushings, Bearings, Heat Exchanger Flanges, Heat Exchanger Headers,
Tanks, Welded Piping Systems, Balls
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
|
Cu(1)
|
Al
|
Fe
|
Mn
|
Ni(2)
|
Si
|
Sn
|
Zn
|
|
Min./Max.
|
Rem.
|
9.0-11.0
|
2.0-4.0
|
1.5
|
4.0-5.5
|
.25
|
.20
|
.30
|
|
Nominal
|
82.0
|
10.0
|
3.0
|
-
|
5.0
|
-
|
-
|
-
|
(1) Cu value includes Ag.
(2) Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min.
C63000 MECHANICAL PROPERTIES
(measured at room temperature, 68 F (20 C)
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness B
|
Rockwell
Hardness C
|
Rockwell
Hardness F
|
Rockwell
Hardness 30T
|
Vickens
Hard.
|
Brinell
Hard. 500
|
Brinell
Hard. 3000
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
Rod
|
|
HR50
|
1
|
|
|
68
|
118
|
75
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
70
|
37
|
0.0
|
|
25.4
|
10
|
TYP
|
20
|
814
|
517
|
-
|
-
|
15
|
98
|
-
|
-
|
-
|
-
|
-
|
-
|
483
|
255
|
0.0
|
|
HR50
|
2.01
|
25.4
|
TYP
|
68
|
100
|
60
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
69
|
38
|
0.0
|
|
51
|
|
|
20
|
689
|
414
|
-
|
-
|
18
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
476
|
262
|
0.0
|
|
HR50
|
2.99
|
25.4
|
TYP
|
68
|
100
|
60
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
65
|
37
|
0.0
|
|
76
|
|
|
20
|
689
|
414
|
-
|
-
|
20
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
448
|
255
|
0.0
|
M30
|
4.02
|
25.4
|
TYP
|
68
|
100
|
60
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
6
|
36
|
0.0
|
|
102
|
|
|
20
|
689
|
414
|
-
|
-
|
15
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
427
|
248
|
0.0
|
|
Bar
|
|
TQ50
|
4.02
|
-
|
-
|
68
|
100
|
50
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
102
|
0
|
TYP
|
20
|
689
|
345
|
-
|
-
|
10
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
HR50
|
2.01
|
-
|
-
|
68
|
100
|
60
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
51
|
10
|
TYP
|
20
|
689
|
414
|
-
|
-
|
15
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
HR50
|
1
|
-
|
-
|
68
|
110
|
62
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
25.4
|
10
|
TYP
|
20
|
758
|
427
|
-
|
-
|
15
|
97
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
M30
|
2.99
|
-
|
-
|
68
|
90
|
50
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
76
|
0
|
TYP
|
20
|
621
|
345
|
-
|
-
|
15
|
96
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|