C92200 Leaded Tin, Navy M Solid Bar
Atlas Bronze offers C92200 Leaded Tin Bronze, Navy M Solid Bar stock. Atlas Bronze offers CDA 922 Solid Bar per ASTM B505 stock in both full bar length and we will cut the material to your desired length as required.
This
material is used in a variety of applications. Typical uses for this
alloy are: Valves, fittings, and pressure containing parts for use up to 550°F.
________________________________________________________________________________________
|
DIAMETER (inches)
|
PART NUMBER
|
|
.8750"
|
9220S-7
|
1.000"
|
9220S-8
|
|
1.125"
|
9220S-9
|
|
1.250"
|
9220S-10
|
|
1.750"
|
9220S-14
|
|
2.000"
|
9220S-16
|
|
2.500"
|
9220S-20
|
|
2.750"
|
9220S-22
|
|
3.000"
|
9220S-24
|
|
3.500"
|
9220S-28
|
|
4.000"
|
9220S-32
|
|
4.500"
|
9220S-36
|
|
5.000"
|
9220S-40
|
|
5.500"
|
9220S-44
|
|
6.000"
|
9220S-48
|
|
|
|
__________________________________________________________________________________________
TYPICALLY USED FOR:
This
material is used in a variety of applications. Typical uses for this
alloy are: Valves, fittings, and pressure containing parts for use up to 550°F.
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
|
|
Cu(1)
|
Al
|
Sb
|
Fe
|
Pb
|
Ni(2)
|
P(3)
|
Si
|
S
|
Sn
|
Zn
|
|
Min./Max.
|
86.0-90.0
|
.005
|
.25
|
.25
|
1.0-2.0
|
1.0
|
.05
|
.005
|
.05
|
5.5-6.5
|
3.0-5.0
|
|
Nominal
|
88.0
|
-
|
-
|
-
|
1.5
|
-
|
-
|
-
|
-
|
6.0
|
4.5
|
(1) In determining Cu min., Cu may be calculated as Cu + Ni.
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.3% min.
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness
|
Vickens
Hard.
|
Brinell
Hard.
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
TYP
|
68
|
40
|
20
|
-
|
-
|
30
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
11
|
0.0
|
|
0.0
|
|
|
20
|
276
|
138
|
-
|
-
|
30
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
76
|
0.0
|
|
As Centrifugal Cast
|
|
M02
|
0.0
|
0
|
SMIN
|
68
|
34
|
16
|
-
|
-
|
22
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
234
|
110
|
-
|
-
|
22
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Continuous Cast
|
|
M07
|
0.0
|
0
|
SMIN
|
68
|
38
|
19
|
-
|
-
|
18
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
262
|
131
|
-
|
-
|
18
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Permanent Mold Cast
|
|
M05
|
0.0
|
0
|
SMIN
|
68
|
34
|
16
|
-
|
-
|
24
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
234
|
110
|
-
|
-
|
24
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
SMIN
|
68
|
34
|
16
|
-
|
-
|
22
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
234
|
110
|
-
|
-
|
22
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.
APPLICABLE SPECIFICATIONS:
NOTE: Information courtesy of Copper.org
|
Product
|
Specification
|
|
Centrifugal
|
ASTM B271
SAE J462, J461
|
|
Continuous
|
ASTM B505
SAE J462, J461
|
|
Fittings
|
ASME B16.24, SB61
ASTM B61
FEDERAL WW-P-460
|
|
Flanges
|
ASME SB61
ASTM B61
FEDERAL WW-P-460
|
|
Ingot
|
ASTM B30
|
|
Sand
|
ASME SB61, SB584
ASTM B61, B584
SAE J461, J462
|
|
Valves
|
MILITARY MIL-V-17547
|
|