C93200 SAE 660 Bearing Bronze
Atlas Bronze offers C93200 Bearing Bronze material, SAE 660 in Solids, Tubes, Cored Bars, Plates, Rectangles, and Castings. This alloy is available as Off-the-Shelf bar stock, Centrifugal Castings (ASTM B271) and Sand Castings (ASTM B584) and Made to Order per your print.
This product is also offered as a specialty product - LARGE BLOCK PLATE, sizes up to 10" thick x 18" wide. The method by which the material is cast will depend on your specification and desired quantity. C93200 SAE 660 bronze material is used in a variety of applications.
Typical uses for this alloy are:
- Fuel Pump Bushings
- Water Pump Bushings,
- Diesel Engine Wrist Pin Bushings,
- Hydraulic Press Stuffing Box,
- Insert Bearings,
- Bearings,
- Thrust Washers,
- Pumps,
|
- Bushings,
- Machine Parts,
- Pump Impellers,
- General Purpose Bushings,
- Fittings,
- Pump Fixtures,
- Machine Tool Bearings
|
How can we help you today with your C93200 needs?
C93200 TYPICALLY USED FOR:
This C93200 SAE 660 bearing bronze material is used in a variety of applications. Typical uses include: Fuel Pump Bushings, Water Pump Bushings, Diesel Engine Wrist Pin Bushings, Hydraulic Press Stuffing Box, Insert Bearings, Bearings, Thrust Washers, Pumps, Bushings, Machine Parts, Pump Impellers, General Purpose Bushings, Fittings, Pump Fixtures, Machine Tool Bearings.
C93200 CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
|
Cu(1)
|
Al
|
Sb
|
Fe
|
Pb
|
Ni(2)
|
P(3)
|
Si
|
S
|
Sn
|
Zn
|
|
Min./Max.
|
81.0-85.0
|
.005
|
.35
|
.20
|
6.0-8.0
|
1.0
|
.15
|
.005
|
.08
|
6.3-7.5
|
1.0-4.0
|
|
Nominal
|
83.0
|
-
|
-
|
-
|
7.0
|
-
|
-
|
-
|
-
|
6.9
|
2.5
|
(1) In determining Cu min., Cu may be calculated as Cu + Ni.
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.0% min.
C93200 MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness
|
Vickens
Hard.
|
Brinell
Hard.
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
TYP
|
68
|
35
|
18
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
16
|
6.0
|
|
0.0
|
|
|
20
|
241
|
124
|
-
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
110
|
8.0
|
|
As Centrifugal Cast
|
|
M02
|
0.0
|
0
|
SMIN
|
68
|
30
|
14
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
207
|
97
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Continuous Cast
|
|
M07
|
0.0
|
0
|
SMIN
|
68
|
35
|
20
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
241
|
138
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
SMIN
|
68
|
30
|
14
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
207
|
97
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
*Fatigue Strength: 100 x 10 6cycles,
unless indicated as [N]X 106.
C93200 APPLICABLE SPECIFICATIONS:
NOTE: Information courtesy of Copper.org
|
Product
|
Specification
|
|
Centrifugal
|
ASTM B271
SAE J462, J461
|
|
Continuous
|
ASTM B505
SAE J461, J462
|
|
Ingot
|
ASTM B30
|
|
Permanent Mold
|
SAE J461, J462
|
|
Sand
|
ASTM B584, B763, B66
SAE J462, J461
|
|