C93600 High Leaded Tin Bronze, MOD SAE 64 Solid Bar
Atlas Bronze offers C93600 High Leaded Tin Bronze, MOD SAE 64 Solid Bar stock. Atlas stocks CDA 936 solid bar as full bar lengths and we will cut to your exact requirements.
Atlas stocks a select variety
of sizes in Rounds and various sizes on a Made to Order basis. Please note that the method in which the material
is
cast will depend on your
size, specification and desired quantity.
__________________________________________________________________________________________
|
DIAMETER (inches)
|
PART NUMBER
|
|
.5000"
|
9360S-4
|
|
.6250"
|
9360S-5
|
|
.7500"
|
9360S-6
|
|
.8750"
|
9360S-7
|
|
1.000"
|
9360S-8
|
|
1.125"
|
9360S-9
|
|
1.250"
|
9360S-10
|
|
1.375"
|
9360S-11
|
|
1.500"
|
9360S-12
|
|
1.625"
|
9360S-13
|
|
1.750"
|
9360S-14
|
|
2.000"
|
9360S-16
|
|
2.125"
|
9360S-17
|
|
2.250"
|
9360S-18
|
|
2.500"
|
9360S-20
|
|
2.750"
|
9360S-22
|
|
3.000"
|
9360S-24
|
|
3.500"
|
9360S-28
|
|
3.750"
|
9360S-30
|
|
4.000"
|
9360S-32
|
|
4.250"
|
9360S-34
|
|
4.500"
|
9360S-36
|
|
4.750"
|
9360S-38
|
|
5.000"
|
9360S-40
|
|
5.500"
|
9360S-44
|
|
6.000"
|
9360S-48
|
|
6.500"
|
9360S-52
|
|
7.000"
|
9360S-56
|
|
8.000"
|
9360S-64
|
|
9.000"
|
9360S-72
|
|
10.00"
|
9360S-80
|
|
11.00"
|
9360S-88
|
|
12.00"
|
9360S-96
|
|
12.50"
|
9360S-100
|
|
|
|
_________________________________________________________________________________________
TYPICALLY USED FOR:
This
material is used in a variety of applications. Typical uses for this
alloy are:
Bushings
for corrosion, lubrication or pressure, Cam Bushings for Diesel
Engines, Crankshaft Main Bearings, Guide Bushings for Piston Rods, Guide
Bushings for Valves, Hydraulic Gland Seals, Locomotive Bearing Parts,
Main Bearings for Presses, Piston Pin Bearings, Pump Sleeves, Rod
Bushings, Rolling Mill Bearings, Sleeve Bushings (for Cranes, etc.),
Bearings for corrosion, lubrication or pressure.
CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
|
|
Cu
|
Al
|
Sb
|
Fe
|
Pb
|
Ni(1)
|
P(2)
|
Si
|
S
|
Sn
|
Zn
|
|
Min./Max.
|
79.0-83.0
|
.005
|
.55
|
.20
|
11.0-13.0
|
1.0
|
.15
|
.005
|
.08
|
6.0-8.0
|
1.0
|
|
Nominal
|
81.0
|
-
|
-
|
-
|
12.0
|
-
|
-
|
-
|
-
|
7.0
|
-
|
(1) Ni value includes Co.
(2) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.3% min.
MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
NOTE: Information courtesy of Copper.org
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness
|
Vickens
Hard.
|
Brinell
Hard.
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
As Centrifugal Cast
|
|
M02
|
0.0
|
0
|
TYP
|
68
|
35
|
21
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
241
|
145
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
-
|
0.0
|
|
M02
|
0.0
|
0
|
SMIN
|
68
|
32
|
16
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
221
|
110
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Continuous Cast
|
|
M07
|
0.0
|
0
|
SMIN
|
68
|
33
|
20
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
227
|
138
|
-
|
-
|
10
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
M07
|
0.0
|
0
|
TYP
|
68
|
35
|
21
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
241
|
145
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
65
|
-
|
-
|
-
|
0.0
|
|
As Permanent Mold Cast
|
|
M05
|
0.0
|
0
|
TYP
|
68
|
35
|
21
|
-
|
|
|