C93700 High Leaded Tin Bronze Bridge Plate per ASTM B22
Atlas Bronze offers C93700 Tin Bronze Bridge Plate, Rectangles and Castings. Atlas stocks a select variety of sizes in Bridge Plate, per ASTM B22. Select shapes & sizes are available Off-the-Shelf, however other sizes are typically cast on a
Made to Order basis. Please note that the method in which the material
is cast will depend on your size, specification and desired quantity.
- 4" thick x 12.2" wide
- 5" thick x 15" wide
- 8" thick x 15-7/8" wide
- 10" thick x 12" wide
C93700 TYPICALLY USED FOR:
This material is used in a variety of applications. Typical uses for this
alloy are:
- Fasteners: Washers for Engines,
- Industrial: Crank Shafts, Bushings, Machine Parts, High Speed, Heavy Load Bearings,
Pumps, Pressure Tight Castings, Impellers, Bushings for high speed and
heavy pressure., Bearings, Bearing Plates, Parts for Steel Mill Maintenance,
- Marine: Large Bearings for Ships
C93700 BRIDGE PLATE CHEMICAL COMPOSITION:
(%max., unless shown as range or min.)
NOTE: Information courtesy of Copper.org
|
|
Cu
|
Al
|
Sb
|
Fe
(1)
|
Pb
|
Ni
(2)
|
P
(3)
|
Si
|
S
|
Sn
|
Zn
|
|
Min./Max.
|
78.0-82.0
|
.005
|
.50
|
.7
|
8.0-11.0
|
.50
|
.10
|
.005
|
.08
|
9.0-11.0
|
.8
|
|
Nominal
|
80.0
|
-
|
-
|
-
|
9.5
|
-
|
-
|
-
|
-
|
10.0
|
-
|
(1) Fe shall be .35% max., when used for steel-backed
(2) Ni value includes Co.
(3) For continuous castings, P shall be 1.5%, max.
Note: Cu + Sum of Named Elements, 99.0% min.
C93700 MECHANICAL PROPERTIES:
(measured at room temperature, 68 F (20 C)
Note: Information courtesy of Copper.org
|
Temper
|
Section
Size
|
Cold
Work
|
Typ/
Min
|
Temp
|
Tensile
Strength
|
Yield
Strength
(0.5% ext.
under load)
|
Yield
Strength
(0.2%
offset)
|
Yield
Strength
(0.05%
offset)
|
El
|
Rockwell
Hardness
|
Vickens
Hard.
|
Brinell
Hard.
|
Shear
Strength
|
Fatigue
Strength*
|
Izod
Impact
Strength
|
|
in.
|
%
|
|
F
|
ksi
|
ksi
|
ksi
|
ksi
|
%
|
B
|
C
|
F
|
30T
|
500
|
500
|
3000
|
ksi
|
ksi
|
ft-lb
|
|
mm.
|
|
|
C
|
MPa
|
MPa
|
MPa
|
MPa
|
|
|
|
|
|
|
|
|
MPa
|
MPa
|
J
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
TYP
|
68
|
35
|
18
|
16
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
60
|
-
|
18
|
13
|
5.0
|
|
0.0
|
|
|
20
|
241
|
124
|
110
|
-
|
20
|
-
|
-
|
-
|
-
|
-
|
60
|
-
|
124
|
90
|
7.0
|
|
As Centrifugal Cast
|
|
M02
|
0.0
|
0
|
SMIN
|
68
|
30
|
12
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
207
|
83
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Continuous Cast
|
|
M07
|
0.0
|
0
|
SMIN
|
68
|
35
|
20
|
-
|
-
|
6
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
241
|
138
|
-
|
-
|
6
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
As Sand Cast
|
|
M01
|
0.0
|
0
|
SMIN
|
68
|
30
|
12
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
|
0.0
|
|
|
20
|
207
|
83
|
-
|
-
|
15
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
-
|
0.0
|
*Fatigue Strength: 100 x 10
6cycles,
unless indicated as [N]X 106.
C93700 APPLICABLE SPECIFICATIONS:
Note: Information courtesy of
Copper.org
|
Product
|
Specification
|
|
Bearings
|
AMS 4827
|
|
Centrifugal
|
AMS 4842
ASTM B271
SAE J462, J461
|
|
Continuous
|
ASTM B505
SAE J461, J462
|
|
Ingot
|
ASTM B30
|
|
Sand
|
AMS 4842
ASME SB584
ASTM B763, B66, B584, B22
SAE J461, J462
|
|